砂浆回弹仪-说明书.doc

HT-20砂浆回弹仪

使

用

说

明

书

上海高致精密仪器

目录

一﹑适用范围································1

二﹑仪器主要技术性能·······················1

三﹑回弹仪的构造原理························1

四﹑仪器的标准状态··························2

五﹑仪器的操作方法··························4

六﹑回弹仪的校验····························5

七﹑维护保养································6

八﹑测试技术································8

(一)一般规定····························8

(二)测强准备过程························9

(三)回弹值的测量与计算·················10

(四)碳化深度值测·······················11

(五)砂浆强度的评定·····················12

(六)评定报告···························15

九﹑HT20型回弹仪的率定·····················16

十﹑附件和技术文件·························18

十一﹑附录·································18

附录一回弹仪检测砌筑砂浆强度报告表·19

附录二砖砌体测区砂浆强度换算表·····20

一、适用范围

HT-20型回弹仪适用于测定工业与民用一般建筑物烧结普通砖砌体中砌筑砂浆的抗压强度。

—25Mpa

二、仪器主要技术性能

HT20型回弹仪的主要技术性能指标如下：

·m)

±0.3〔mm〕

±0.10〔N〕

4．弹击杆球面曲率半径SR25±1.0〔mm〕

5．回弹仪在钢砧上率定平均回弹值Rm74±2

6．外形尺寸?60×280mm

7．重量≈1kg

三、回弹仪的构造原理

HT20型回弹仪的构造原理是，利用砂浆外表硬度与其抗压强度之间的相关关系，建立砂浆强度与回弹值和碳化深度值的回归方程和曲线并用来评定砂浆的强度。

HT20型回弹仪主要由弹击系统，示值系统和仪壳部件等组成其构造如图1所示：

弹击系统中的弹击杆1主要是将弹击锤14的动能传给被测砂浆试件2，并将冲击后的回弹能量传给弹击锤，使其回弹一定的距离，弹击拉簧16主要是储存能量并赋予弹击锤14，而弹击锤14既是能量的携带件，又是弹击系统与示值系统间的联系元件。即示值系统中指针滑块4所指示的回弹值，是弹击锤14冲击弹击杆1后回弹时带动其移动的距离。

示值系统均固定在仪器壳体3上。保持其与弹击系统的相对位置和运动关系。示值系统指针回零是通过压缩弹簧12驱动导向法兰8致使弹击系统恢复非弹击状态的同时，将其带到设定的位置而实现的。

仪器尾盖11上的调整螺栓是用来控制弹击锤14的冲程〔脱钩点〕和起跳点，因此，一但调整螺栓的高度经确定，那么不允许随意改变。

四、仪器的标准状态

回弹法测强关键问题是仪器的一致性。因此，统一回弹仪的技术标准是非常必要的，现将回弹仪标准状态的具体要求规定如下：

1．当回弹仪水平弹击时，弹击锤脱钩瞬间所具有的动能应为0.196J〔0.02kgf.m〕。

2．弹击锤的冲程75mm，锤发射〔即脱钩〕时指针滑块上的刻表对应于刻度尺“100”处，弹击锤回跳时指针滑块上的刻线对应于刻度尺“0”位。

±0.5mm在弹击锤与弹击杆碰撞瞬间，弹击拉簧，处于自由状态。

±0.1N。

5．弹击杆前端弹击球面的曲率半径SR25mm。

6．在洛氏硬度HRC58-62的钢砧上垂直向下率定，每率定5次旋转弹击杆90o，共分四次旋转。每一个方向取后三次且读数稳定的回弹值进行平均，平均回弹值应为Rm=74±2。

五、仪器的操作方法

正确使用与操作回弹仪才能取得可靠的测试效果。

1．在测试过程中回弹仪的轴线应始终垂直于砂浆外表，将回弹仪的弹击杆顶住砂浆外表，轻压回弹仪使按钮松开弹击杆伸出仪壳，并使挂钩挂上弹击锤。

2．将已伸出的弹击杆对砂浆外表均匀施压，待到达即将脱钩时，调整好回弹仪对测试外表的垂直度再轻微施压使弹击锤脱钩进行弹击，重复上述动作，在一个测点上连续弹击三次，且不能移位，然后读取记录第三次在刻度尺上标示的某一回弹值，如条件不利于读取回弹值时可按下按钮，锁住机芯，将回弹仪