汽车涂装面漆颗粒分析和防治.docx

现代涂料与涂装TechnologyandExperienceCommunion‖技术与经验交流

汽车涂装面漆颗粒分析和防治

杨东，李平，李淑贞

(北京汽车集团越野车有限公司，北京101300)

摘要：对汽车面漆涂层颗粒进行分析汇总，明确了面漆涂层颗粒的主要来源是色漆漆渣、清漆漆渣和打磨灰尘。生产现场采取调整喷漆室风平衡、强化喷涂设备及工装工具的清洁、密闭喷漆前的敞开区域、规范标准作业流程等措施，改善了涂装面漆颗粒问题，据统计单台面漆颗粒数下降了64%，提升了涂装外观质量及生产线工作效率。

关键词：面漆涂层；颗粒；外观质量

中图分类号：TQ639文献标志码：B文章编号：1007-9548(2021)05-0029-03

AnalysisandPreventionoftheParticlesofAutomobileFinishingCoating

YANGDong,LIPing,LIShu-zhen

(BAICGroupOff-roadVehicleCo.,Ltd.,Beijing101300,China)

Abstract:Coatingparticlesofautomotivetopcoatswereanalyzedandsummarized,andthemainsourcesoftopcoatcoatingparticleswerepaintresidue,varnishresidueandgrindingdust.Theproductionsitemeasureswereadoptedsuchasadjustingtheairbalanceofthespraybooth,strengtheningthecleaningofsprayingequipmentandtoolingtools,sealingtheopenareabeforespraying,andstandardizingstandardoperatingprocedurestoimprovepaintparticleproblem.Accordingtostatistics,thenumberoftoppaintparticlesonasingletablehasdroppedby64%,improvedtheappearancequalityofpaintingandtheefficiencyofproductionline.

Keywords:topcoatcoating;particles;appearancequality

0引言

车身漆膜颗粒多造成精修工作量大，降低生产效率，影响涂装质量。鉴于面漆涂层颗粒缺陷来源复杂，必须对面漆涂层中的该缺陷进行分析汇总，追溯缺陷来源，明确缺陷起因，逐一分析并采取相对应的解决方法，从根本上解决面漆涂层颗粒缺陷。

1面漆涂层颗粒的分类

根据现场生产经验，我们把面漆涂层颗粒分为以下几大类。

1.1环境颗粒

由外界环境引起的颗粒缺陷，具体指喷漆作业环境，如喷漆室风压不均衡导致的漆雾四散、喷涂设备

—

收稿日期：2020-08-11

作者简介：杨东(1983—)，男，本科，工程师，主要从事汽车涂装工艺管理工作。E-mail：yangdong@。

及工装工具等附着漆雾、敞开区域的尘埃粒子飘落、车身残留的打磨灰尘、烘干炉清洁度不合格等。

1.2涂料颗粒

由涂料本身所导致的面漆漆膜颗粒缺陷，主要是由于输调漆管路的油漆沉积、喷涂系统中涂料雾化效果不好等因素造成。

1.3残胶颗粒

涂胶作业时车身上的残胶所导致的面漆颗粒缺陷，主要是由于涂装焊缝密封胶、底涂胶涂胶过程中的残胶飞溅所导致。

1.4前处理电泳颗粒

残留在白车身上的铁粉、焊渣在前处理未能冲洗干净，导致形成电泳颗粒。这类颗粒在后续电泳打磨时未去除干净，喷漆后该部位呈现面漆颗粒缺陷。

1.5静电颗粒

高压喷涂时由于静电因素所导致的面漆漆膜颗