两种不同造孔剂对粉煤灰-黄土基支撑体性能的影响.pdfVIP

两种不同造孔剂对粉煤灰-黄土基支撑体性能的影响

摘要：以粉煤灰、黄土为混合骨料，甲基纤维素作粘结剂,采用挤压成型法和固态粒子烧结法制备陶瓷膜支撑体，

探究淀粉和聚甲基丙烯酸甲酯两种造孔剂对支撑体的孔隙形成、抗折强度、酸碱腐蚀率、物相组成、显微结构及纯

水通量等性能的影响。结果表明,聚甲基丙烯酸甲酯添加量为15%时，各项参数基本优于淀粉添加量为10%时支

撑体的各项表征,并且其成品内部孔隙均一,分布较为均匀,孔径均在6μm左右，酸碱质量损失率分别为0.24%/

0.19%，孔隙率为35%，抗折强度为30MPa，支撑体纯水通量为9523.28L/（m²，h·MPa）。

关键词：黄土；粉煤灰；造孔剂；纯水通量；抗折强度

Effectsoftwodifferentporeformingagentsonthe

propertiesofflyashloessfoundationsupport

Abstract:Theceramicfilmsupportswerepreparedbyextrusionandsolidparticlesinteringmethodsusing

flyashandloessasmixedaggregatesandmethylcelluloseasbinder,andtheeffectsoftwoporogenica-

gents,starchandpolymethylmethacrylate,onthepropertiesofthesupports,suchasporeformation,flexur-

alstrength,acid-basecorrosionrate,phasecomposition,microstructureandpurewaterflux,wereinvesti-

gated.Theresultsshowedthattheparametersofpolymethylmethacrylateaddedat15%werebasically

betterthanthecharacterizationoftheproppantat10%starchaddition,andtheinternalporesofthefin-

ishedproductswerehomogeneousandmoreuniformlydistributed,withtheporesizearound6μm,the

acid-basemasslossratewas0.24%/0.19%,theporositywas35%,theflexuralstrengthwas30MPa,

andthepurewaterfluxoftheproppantwas9523.28L/(m².h·MPa),respectively.

Keywords:loess;flyash;poreformingagent;purewaterflux;flexuralstrength

无机陶瓷膜因其过滤效率较高、耐高温、易清分见表1；粉煤灰，购于西安市某热电厂，其化学成

洗再生等优点在诸多领域受到广泛应用[13]。目前分见表2;甲基纤维素（MC）、聚甲基丙烯酸甲酯

制备陶瓷膜支撑体的原料均成本较高，其商业化应(PMMA）、淀粉均为分析纯。

用受到限制[4-7]。降低成本成为了学者的研究重表1粉煤灰的化学成分表

Table1B

点13-2]。粉煤灰作为工业固体废弃物，其资源化利Basicchemicalcompositionofflyash

物质名称含量/%

用也是目前函待解决的问