(2162)--不同橡胶在SBS改性沥青防水卷材用涂盖料中的应用研究.pdf

不同橡胶在SBS 改性沥青防水卷材用 涂盖料中的应用研究 摘要：采用不同橡胶与SBS 聚合物共混改性沥青制备SBS 改性沥青防水卷材用涂盖料，研究了不同橡胶对涂盖料耐热 性、耐低温性和接缝剥离强度的影响。结果表明: 顺丁烯橡胶有助于提升涂盖料的耐低温性能，丁腈橡胶有助于提升涂 盖料的接缝剥离强度，热塑性聚烯烃橡胶和三元乙丙橡胶对改性沥青防水卷材用涂盖料的性能改善作用不明显。 关键词：SBS 改性沥青防水卷材；橡胶；改性沥青涂盖料；接缝剥离强度 + 文章编号：1007-497X （2019）-08-0019-03 中图分类号：TU57 3 ；TU502 文献标志码：A Application Study on Different Rubber in Coating Material of SBS Modified Asphalt Waterproofing Membrane Sun Yanwei （Keshun Waterproof Technology Co., Ltd., Foshan, Guangdong 528303, China） Abstract: Coating material of SBS modified asphalt waterproofing membrane is prepared by blending SBS modified asphalt with different rubber, and the influences of different rubbers on heat resistance, low temperature resistance and joint peeling strength of the coating materials are investigated. The results show that: butylene rubber can improve the low temperature resistance of the coating material, nitrile rubber can help improve the joint peeling strength of the coating material, and performance improvement effect of thermoplastic polyolefin rubber and EPDM rubber is not obvious. Key words: SBS modified asphalt waterproofing membrane; rubber; modified asphalt coating; joint peeling strength 0 前言 时也带来生产加工困难及后期储存、应用稳定性差的 SBS 改性沥青防水卷材用涂盖料一般是以SBS 问题。针对上述问题，大量学者研究采用两种或两种 作为主要的聚合物改性剂，通过简单机械共混制备而 以上的改性剂，优势互补，以期提升普通改性沥青的 成，SBS 作为热塑性弹性体，大幅改善了沥青的高低 性能。类似研究有采用树脂类（EVA、PE 等）和无机酸 [1] 温性能和温度敏感性 。但单一聚合物改性沥青也存 类（PPA）改性剂与SBS 复合改性沥青，显著提升了基 在诸多问题[2-3] ，最突出的是聚合物与基质沥青的相容 质沥青的耐热性、热稳