不锈钢带钢连续退火炉前沿综述.doc

不锈钢带钢连续退火炉前沿综述 陈 莉 奥地利安德里斯股份有限公司上海代表处金属部 上海市 邮编：200021 魏文华 西马克梅尔工程（中国）有限公司销售部 上海市 邮编：201100 中文摘要：随着不锈钢市场的发展，世界上的一些先进技术也传入了中国。尤其是对于不锈钢带钢生产线的连续作业机组，更要求多工艺集成后的高效率、高品质生产。本文就不锈钢带钢连续生产作业线中的各种比较典型的先进的退火炉装备及其工艺进行了比较、阐述，尤其重点介绍了不锈钢带钢连续退火酸洗线以及不锈钢带钢光亮退火线的先进技术。 中文关键词：不锈钢带钢、连续生产线、连续退火酸洗线、光亮退火炉。 Advanced Stainless Steel Strip Continuous Annealing Line Chen Li Andritz Shanghai Representative Office Shanghai of China PC:200021 Wei Wenhua SMS Meer Engineering (China) Ltd. Shanghai of China PC:201100 Summary: Along with stainless steel development on market, some of advanced technique goes into China. Especially for the stainless steel strip production continuous line, the more complicate the more high efficiency and high quality required. This article is focus on comparing various typical continuous annealing furnaces by equipment and processing. Mostly it is on stainless steel strip continuous annealing and pickling line and stainless steel strip bright annealing line. Key words: Stainless steel strip, continuous line, continuous annealing and pickling line, bright annealing line. 基金项目和项目编号：无 第一作者简介：陈莉，1970年出生，女。本科学历毕业于东北大学，中级工程师资历，现任安德里斯公司上海办 项目经理。E-mail: li.chen@ 手机[正文] 不锈钢带钢可以采用热轧或冷轧进行加工。轧制操作将增大带钢的硬度值，再通过必要的退火操作去软化材料以便进入后续工艺。 退火工艺的操作并不局限于材料相应的品质标准，同样也取决于特殊的用户要求。 不锈钢带钢的性质特征在欧洲标准EN10 088-2中进行了规定，带钢表面的品质也有标准可寻，见德国标准DIN17740。 对于不锈钢热轧板的铁素体钢，通常是在罩式退火路的全氢气氛保护下进行退火的，而其他不锈钢的退火则采用连续退火工艺。 退火酸洗线（Annealing and Pickling line /APL）：加热过程采用直接火焰加热式炉用于软化在之前由于轧制工艺而变硬的材料。充满氧气的环境下进行退火工艺所产生的表面氧化层将在随后的在线酸洗工艺中被去除，产生出干净而无氧化层的表面。带钢既可以作为最终产品进行销售，也可以进一步作为冷轧的原料进行使用。 光亮退火线（Bright Annealing line /BAL）：热处理将在一个H2/N2 气氛、露点控制在-40~-60 C范围的情况下进行。目的是维持由特殊的冷轧工艺所获得的光洁、光亮的带钢表面。避免再度氧化和污染。 退火工艺按材料大致可分为两类 ● 奥氏体钢，带钢的目标温度为 1080 ~ 1150 C ● 铁素体钢，带钢的目标温度为 780 ~ 870 C 总的来讲，要高效的获得带钢所期望的最终温度值，而不再需要进一步的均热过程，退火后带钢晶体颗粒的目标值为ASTM 8 ~ 9级（约颗粒度为 15 ~ 22 μm ）。由于铁素体带钢的特性，可以通过在线检测剩磁的方法被鉴定出来，这种检测方法也被用于高效的动态工艺控制。 加热后，带钢将在冷却段采用对流方式进行冷却，对于不同的产品，APL炉子段的冷却方式可以是空冷、水冷或空冷加水冷（雾冷）的混合方式。 在光亮退火炉中，带钢必须在保护气氛下被冷却，以避免氧化或污染的再发生。 为避免