攀枝花学院本科毕业设计（论文） 多孔二氧化钛光催化性能评价条件研究 院 （系）： 生物与化学工程学院 专 业： 化学工程与工艺 学生姓名： 陈俊恩 学 号： 200510901104 指导教师： 田从学 副教授 2009.06.08 摘要 TiO2是一种能够净化环境的绿色功能材料,它不仅具有氧化能力强，无选择性，能耗低，无二次污染，降解完全等优点,而且还具有价廉、无毒、可长期使用等特点,所以它成为近年来光催化技术研究的热点并且广泛用于催化剂、颜料等领域。（简称MB）考察了不同光催化条件下二氧化钛对亚甲基蓝降解率的影响吸收波长666nm，亚甲基蓝溶液pH5.0，甲基蓝溶液浓度，催化剂用量g/L。亚甲基蓝; 多孔二氧化钛; 催化剂用量；pH值；光催化 ABSTRACT Titania is a green functional materials capable of decontaminating the environment, due to, its merits of strong oxidizing ability, non-selectivity, low energy consumption, no secondary pollution, degradation completely, etc., as well as cheap, non-toxic, long-term photostability in recent yearsit . Therefore, in recent years it has become research focus of photocatalytic technology and it is widely used in catalyst, pigmentsand and other fields. In this paper, metatitanic acid used as raw material, photocatalytic experiments carried out in different conditions to investgate the effects of ??? on porous titania structure and photocatalytic performances. The as-prepared powders were characterized by XRD, FT-IR, paritcle size distribution test, specific surface area measurement, etc. 后面自己修改翻译The photocatalytic property of the prepared porous titanium was evaluated by a model of degrading MB , And the optimal experimental conditions are absorbed wave length of 666nm, pH=5.0 and catalyst dosage of 1.0 g/L. Key words: Methylene blue；porous titania; catalyst dosage; pH value; photocatalysis  目 录 摘要 I ABSTRACT II 1绪论 1 1.1课题研究背景 1 1.2课题研究意义 1 1.3光催化材料的应用现状 2 1.4光催化原理 4 1.5课题研究思路 7 2实验部分 7 2.1实验药品与试验仪器 7 2.1.1实验药品 7 2.1.2实验设备、仪器及装置图 8 2.2实验步骤 9 2.3样品的分析检测 10 2.3.1粒度分析 10 2.3.2红外光谱分析 11 2.3.3 XRD衍射分析 11 2.3.4 扫描电镜测试（SEM） 12 2.3.5比表面积测定(BET) 12 3结果分析与讨论 13 3.1吸收波长的影响 13 3.2 MB浓度的影响 13 3.3 初始浓度的影响 14 3.4 pH的影响 15 3.5 TiO2用量的影响 16 3.6 时间对MB降解率的影响 17 3.7 煅烧温度对降解率的影响 18 3.8表征测试分析 19 3.8.1 粒度分析 19 3.8.2 红外光谱分析 20 3.8.3 XRD衍射分析 21 3.8.4 扫描电镜分析 21 3.8.5 比表面积分析 22 4 结论与展望 24 4.1结论 24 4.2展望 24 参